MT409

Corrosion engineering Laboratory

L T P C
0 0 3 2

 

 

 

 

Copper electroplating, electroless plating, anodizing of aluminum, corrosion rate determination by weight loss method (with and without inhibitor),

Corrosion rate by electrical resistance method, corrosion rate by potentiostatic polarization experiment (a) Tafel method and   (b) LPR method, atmospheric/environmental corrosion (using colour indicator method),

Galvanic corrosion, pitting corrosion, stress corrosion cracking,

IGC susceptibility tests for stainless steels, salt spray test, coating thickness measurements,

Cathodic protection, high temperature corrosion.